Special Issue on Flexible and Wearable Electronics: from Materials to Applications

Engineering in-plane silicon nanowire springs for highly stretchable electronics

Zhaoguo Xue, Taige Dong, Zhimin Zhu, Yaolong Zhao, Ying Sun and Linwei Yu

+ Author Affiliations

 Corresponding author: Linwei Yu, yulinwei@nju.edu.cn

PDF

Turn off MathJax

Abstract: Crystalline silicon (c-Si) is unambiguously the most important semiconductor that underpins the development of modern microelectronics and optoelectronics, though the rigid and brittle nature of bulk c-Si makes it difficult to implement directly for stretchable applications. Fortunately, the one-dimensional (1D) geometry, or the line-shape, of Si nanowire (SiNW) can be engineered into elastic springs, which indicates an exciting opportunity to fabricate highly stretchable 1D c-Si channels. The implementation of such line-shape-engineering strategy demands both a tiny diameter of the SiNWs, in order to accommodate the strains under large stretching, and a precise growth location, orientation and path control to facilitate device integration. In this review, we will first introduce the recent progresses of an in-plane self-assembly growth of SiNW springs, via a new in-plane solid-liquid-solid (IPSLS) mechanism, where mono-like but elastic SiNW springs are produced by surface-running metal droplets that absorb amorphous Si thin film as precursor. Then, the critical growth control and engineering parameters, the mechanical properties of the SiNW springs and the prospects of developing c-Si based stretchable electronics, will be addressed. This efficient line-shape-engineering strategy of SiNW springs, accomplished via a low temperature batch-manufacturing, holds a strong promise to extend the legend of modern Si technology into the emerging stretchable electronic applications, where the high carrier mobility, excellent stability and established doping and passivation controls of c-Si can be well inherited.

Key words: c-Si nanowiresin-plane solid-liquid-solidself-assemblystretchable electronics



[1]
Kim J, Salvatore G A, Araki H, et al. Stretchable optoelectronic systems for wireless optical characterization of the skin. Sci Adv, 2016, 2: e1600418 doi: 10.1126/sciadv.1600418
[2]
Xu B, Rogers J A. Mechanics-driven approaches to manufacturing—A perspective. Extrem Mech Lett, 2016, 7: 44 doi: 10.1016/j.eml.2015.12.012
[3]
Kim D H, Ghaffari R, Lu N, et al. Flexible and stretchable electronics for biointegrated devices. Ann Rev Biomed Eng, 2012, 14: 113 doi: 10.1146/annurev-bioeng-071811-150018
[4]
Hussain A M, Hussain M M. CMOS-technology-enabled flexible and stretchable electronics for internet of everything applications. Adv Mater, 2016, 28: 4219 doi: 10.1002/adma.v28.22
[5]
Hammock M L, Chortos A, Tee B C K, et al. The evolution of electronic skin (e-skin): a brief history, design considerations, and recent progress. Adv Mater, 2013, 25: 5997 doi: 10.1002/adma.201302240
[6]
Cheng T, Zhang Y, Lai. Stretchable thin-film electrodes for flexible electronics with high deformability and stretchability. Adv Mater, 2015, 27: 3349 doi: 10.1002/adma.v27.22
[7]
Wang Y, Zhu C, Pfattner R, et al. A highly stretchable, transparent, and conductive polymer. Sci Adv, 2017, 3: e1602076 doi: 10.1126/sciadv.1602076
[8]
Roberts M E, Mannsfeld S C B, Stoltenberg R M, et al. Flexible, plastic transistor-based chemical sensors. Org Electron, 2009, 10: 377 doi: 10.1016/j.orgel.2008.12.001
[9]
Sokolov A N, Roberts M E, Bao Z. Fabrication of low-cost electronic biosensors. Mater Today, 2009, 12: 12 doi: 10.1016/S1369-7021(09)70247-0
[10]
Arias A C, MacKenzie J D, McCulloch I, et al. Materials and applications for large area electronics: solution-based approaches. Chem Rev, 2010, 110: 3 doi: 10.1021/cr900150b
[11]
Lei Z, Wang Q, Sun S, et al. A bioinspired mineral hydrogel as a self-healable, mechanically adaptable ionic skin for highly sensitive pressure sensing. Adv Mater, 2017, 29: 1700321 doi: 10.1002/adma.201700321
[12]
Lin P, Yan F. Organic thin-film transistors for chemical and biological sensing. Adv Mater, 2012, 24: 34 doi: 10.1002/adma.201103334
[13]
Wang L, Liu P, Guan P, et al. In situ atomic-scale observation of continuous and reversible lattice deformation beyond the elastic limit. Nat Commun, 2013, 4: 2413 doi: 10.1038/ncomms3413
[14]
Wang L, Zheng K, Zhang Z, et al. Direct atomic-scale imaging about the mechanisms of ultralarge bent straining in Si nanowires. Nano Lett, 2011, 11: 2382 doi: 10.1021/nl200735p
[15]
Zheng K, Han X, Wang L, et al. Atomic mechanisms governing the elastic limit and the incipient plasticity of bending Si nanowires. Nano Lett, 2009, 9: 2471 doi: 10.1021/nl9012425
[16]
Zhu Y, Xu F, Qin Q, et al. Mechanical properties of vapor-liquid-solid synthesized silicon nanowires. Nano Lett, 2009, 9: 3934 doi: 10.1021/nl902132w
[17]
Khang D Y, Jiang H, Huang Y, et al. A stretchable form of single-crystal silicon for high-performance electronics on rubber substrates. Science, 2006, 311: 208 doi: 10.1126/science.1121401
[18]
Kim H W, Shim S H. Helical nanostructures of SiOx synthesized through the heating of Co-coated substrates. Appl Surf Sci, 2007, 253: 3664 doi: 10.1016/j.apsusc.2006.07.083
[19]
Zhang H F, Wang C M, Buck E C, et al. Synthesis, characterization, and manipulation of helical SiO2 nanosprings. Nano Lett, 2003, 3: 577 doi: 10.1021/nl0341180
[20]
Swain B S, Lee S S, Lee S H, et al. Transformation of silicon nanowires to nanocoils by annealing in reducing atmosphere. J Cryst Growth, 2011, 327: 276 doi: 10.1016/j.jcrysgro.2011.06.018
[21]
Tang Y H, Zhang Y F, Wang N, et al. Morphology of Si nanowires synthesized by high-temperature laser ablation. J Appl Phys, 1999, 85: 7981 doi: 10.1063/1.369389
[22]
Tian B, Xie P, Kempa T J, et al. Single-crystalline kinked semiconductor nanowire superstructures. Nat Nano, 2009, 4: 824 doi: 10.1038/nnano.2009.304
[23]
Lugstein A, Steinmair M, Hyun Y J, et al. Pressure-induced orientation control of the growth of epitaxial silicon nanowires. Nano Lett, 2008, 8: 2310 doi: 10.1021/nl8011006
[24]
Musin I R, Filler M A. Chemical control of semiconductor nanowire kinking and superstructure. Nano Lett, 2012, 12: 3363 doi: 10.1021/nl204065p
[25]
Schmidt V, Wittemann J V, Senz S, et al. Silicon nanowires: a review on aspects of their growth and their electrical properties. Adv Mater, 2009, 21: 2681 doi: 10.1002/adma.200803754
[26]
Wagner R S, Ellis W C. Vapor-liquid-solid mechanism of single crystal growth. Appl Phys Lett, 1964, 4: 89 doi: 10.1063/1.1753975
[27]
Xu F, Lu W, Zhu Y. Controlled 3D buckling of silicon nanowires for stretchable electronics. ACS Nano, 2011, 5: 672 doi: 10.1021/nn103189z
[28]
Kim D H, Ahn J H, Choi W M, et al. Stretchable and foldable silicon integrated circuits. Science, 2008, 320: 507 doi: 10.1126/science.1154367
[29]
Jang K I, Li K, Chung H U, et al. Self-assembled three dimensional network designs for soft electronics. Nat Commun, 2017, 8: 15894
[30]
Sepulveda A C C, Cordero M S D, Carreño A A A, et al. Stretchable and foldable silicon-based electronics. Appl Phys Lett, 2017, 110: 134103 doi: 10.1063/1.4979545
[31]
Rojas J P, Arevalo A, Foulds I G, et al. Design and characterization of ultra-stretchable monolithic silicon fabric. Appl Phys Lett, 2014, 105: 154101 doi: 10.1063/1.4898128
[32]
Kim J, Lee M, Shim H J, et al. Stretchable silicon nanoribbon electronics for skin prosthesis. Nat Commun, 2014, 5: 5747 doi: 10.1038/ncomms6747
[33]
Pevzner A, Engel Y, Elnathan R, et al. Confinement-guided shaping of semiconductor nanowires and nanoribbons: " writing with nanowires”. Nano Lett, 2012, 12: 7 doi: 10.1021/nl201527h
[34]
Gonzalez M, Axisa F, Bulcke M V, et al. Design of metal interconnects for stretchable electronic circuits. Microelectron Rel, 2008, 48: 825 doi: 10.1016/j.microrel.2008.03.025
[35]
Vanfleteren J, Gonzalez M, Bossuyt F, et al. Printed circuit board technology inspired stretchable circuits. MRS Bull, 2012, 37: 254 doi: 10.1557/mrs.2012.48
[36]
Yu L, Alet P J, Picardi G, et al. An in-plane solid-liquid-solid growth mode for self-avoiding lateral silicon nanowires. Phys Rev Lett, 2009, 102: 125501 doi: 10.1103/PhysRevLett.102.125501
[37]
Yu L, P Roca i Cabarrocas. Initial nucleation and growth of in-plane solid-liquid-solid silicon nanowires catalyzed by indium. Phys Rev B, 2009, 80: 085313 doi: 10.1103/PhysRevB.80.085313
[38]
Yu L, P Roca i Cabarrocas. Growth mechanism and dynamics of in-plane solid-liquid-solid silicon nanowires. Phys Rev B, 2010, 81: 085323 doi: 10.1103/PhysRevB.81.085323
[39]
Scarontich I, Car R, Parrinello M. Amorphous silicon studied by ab initio molecular dynamics: preparation, structure, and properties. Phys Rev B, 1991, 44: 11092 doi: 10.1103/PhysRevB.44.11092
[40]
Roorda S, Doorn S, Sinke W C, et al. Calorimetric evidence for structural relaxation in amorphous silicon. Phys Rev Lett, 1989, 62: 1880 doi: 10.1103/PhysRevLett.62.1880
[41]
Yu L P. Morphology control and growth dynamics of in-plane solid–liquid–solid silicon nanowires. Physica E, 2012, 44: 1045 doi: 10.1016/j.physe.2011.06.005
[42]
Xue Z, Xu M, Li X, et al. In-plane self-turning and twin dynamics renders large stretchability to mono-like zigzag silicon nanowire springs. Adv Func Mater, 2016, 26: 5352 doi: 10.1002/adfm.201600780
[43]
Xue Z, Xu M, Zhao Y, et al. Engineering island-chain silicon nanowires via a droplet mediated Plateau-Rayleigh transformation. Nat Commun, 2016, 7: 12836 doi: 10.1038/ncomms12836
[44]
Shin N, Chi M, Howe J Y, et al. Rational defect introduction in silicon nanowires. Nano Lett, 2013, 13: 1928 doi: 10.1021/nl3042728
[45]
Algra R E, Verheijen M A, Borgstrom M T, et al. Twinning superlattices in indium phosphide nanowires. Nature, 2008, 456: 369 doi: 10.1038/nature07570
[46]
Li X, Wei X, Xu T, et al. Remarkable and crystal-structure-dependent piezoelectric and piezoresistive effects of InAs nanowires. Adv Mater, 2015, 27: 2852 doi: 10.1002/adma.v27.18
[47]
Li X, Wei X L, Xu T T, et al. Mechanical properties of individual InAs nanowires studied by tensile tests. Appl Phys Lett, 2014, 104: 103110 doi: 10.1063/1.4868133
[48]
Xu M, Xue Z, Yu L, et al. Operating principles of in-plane silicon nanowires at simple step-edges. Nanoscale, 2015, 7: 5197 doi: 10.1039/C4NR06531J
[49]
Yu L, Moustapha O, Oudwan M, et al. Guided growth of in-plane lateral SiNWs led by indium catalysts. Mater Res Soc Symp Proc, 2009, 1178E: AA07
[50]
Yu L, Oudwan M, Moustapha O, et al. Guided growth of in-plane silicon nanowires. Appl Phys Lett, 2009, 95: 113106 doi: 10.1063/1.3227667
[51]
Yu L, Chen W, O'Donnell B, et al. Growth-in-place deployment of in-plane silicon nanowires. Appl Phys Lett, 2011, 99: 203104 doi: 10.1063/1.3659895
[52]
Xu M, Wang J, Xue Z, et al. High performance transparent in-plane silicon nanowire Fin-TFTs via a robust nano-droplet-scanning crystallization dynamics. Nanoscale, 2017, 9: 10350 doi: 10.1039/C7NR02825C
[53]
Chen W, Yu L, Misra S, et al. Incorporation and redistribution of impurities into silicon nanowires during metal-particle-assisted growth. Nat Commun, 2014, 5: 4134
[54]
Xue Z, Sun M, Zhao Y, et al. Deterministic line-shape programming of silicon nanowires for extremely stretchable springs and electronics. Nano Lett, 2017, 17: 7638
[55]
O'Mara W, Herring R B, Hunt L P. Handbook of semiconductor silicon technology. Crest Publishing House, 2007
Fig. 1.  (Color online) Schematic illustrations for the comparison of (a) the crystal pulling of thick bulk c-Si ingot at high temperature, to (b) the self-assembly growth of Si nanowires (SiNWs) at a much lower growth temperature, with yet a new possibility to engineer the line-shape for extra flexibility and stretchability.

Fig. 2.  (Color online) Typical SEM images of the low melting point metal (indium or tin) droplet catalyzed (a) vertical VLS growth of standing silicon nanowires (SiNWs) in a gaseous feeding environment, compared to (b) the in-plane solid–liquid–solid (IPSLS) growth of lateral SiNWs that take in amorphous Si (a-Si) thin film as precursor. The upper panel illustration in (b) depicts the driving energy for the IPSLS growth, where Si atoms in a-Si have a higher Gibbs energy, with respect to crystalline Si phase. While both growth mechanisms have a solid–liquid (S–L) rear deposition interface, the front absorption interface in IPSLS growth is relatively hard, as it is also of S (a-Si)–L (liquid droplet) type, which is remarkably different from the soft gas–liquid (G–L) front interface in VLS growth. This results in a strong front-rear interface interaction during an in-plane growth, as a basis for geometry engineering of the in-plane SiNWs. Adapted from Ref. [3638, 41].

Fig. 3.  (Color online) Fabrication procedure for the in-plane SiNWs, which involves (a) H2 plasma treatment for catalyst droplet formation, (b) a-Si:H layer coating as precursor and (c) in-situ annealing in vacuum for in-plane growth. (d) shows the typical SEM image of the free in-plane SiNWs, while (e) summarizes the overall thermal budget for each fabrication step. Adapted from Ref. [36].

Fig. 4.  (Color online) (a)–(c) show the typical SEM images of the in-plane SiNWs, grown with different balance condition gauged by a factor of $\eta -{d_{\rm c}}/{h_{\rm a}}$ . (d) plot the interface speeds of the front absorption and the rear deposition interfaces, as a function of the Si atom concentration dissolved in the liquid catalyst droplet, with a classification of three zones for the formation of straight or bent in-plane SiNWs[38, 41].

Fig. 5.  (Color online) (a), (c)–(e) show the typical SEM images of the zigzag SiNWs, with an enlarged view of the final end of the in-plane SiNW presented in the inset of (a), where the remnant a-Si:H layer has been selectively etched off. (b) illustrates the in-plane turning twinning sequence in a Si [ $11{\bar 2} $ ]-centered stereographic projection mapping. (d) shows three snapshots of the in-plane growth of SiNWs at different time, during annealing growth upon a heating stage in SEM system. (f) presents a close SEM view of a zigzag SiNW segment, with the extracted growth direction deviation (away from the general Si <211> direction) being plotted in (e) as a function of the length of SiNW. Adapted from Ref. [ 42].

Fig. 6.  (Color online) HR-TEM characterizations of a segment of a zigzag SiNW: Fourier transform diffraction patterns of different segments for Domain A are presented in (a) and (c) [or Domain B in (e) and (g)]; (b) and (f) show the local HR-TEM lattice images of the SiNW segment at places marked by the green or red spots, respectively; (d) shows the reconstruction of the whole SiNW by adding up local HR-TEM images, with a series of parallel white dash-lines marking the locations of twin planes, and green or red arrows indicating the local growth orientation in Domain A or B[42].

Fig. 7.  Stress-strain testing of the zigzag SiNWs spring: (a) SEM image of in-situ stress-strain testing setup with of a segment of zigzag SiNWs mounted on the tip of a nano probe and to the end of a cantilever, while (b) shows the linear elastic response[42] .

Fig. 8.  (Color online) (a) and (b) show a comparison of the guided growth of in-plane SiNWs, with the aid of simple step edge to the drawing of straight lines or regular circles with the use of rulers and compass. The SEM images show that, while the free SiNWs are irregular, the guided SiNWs faithfully follow the straight and turning edges of SiNx steps. (c)–(e) illustrates the implementation steps of the guided growth of SiNWs, where the step edge is provided by patterning SiNx dielectric layer crossing the indium stripes. Adapted from Ref. [48].

Fig. 9.  (Color online) (a) shows the key dimensions of a liquid catalyst droplet in a SEM image, while (b) depicts the 4 different contact profiles during a guided growth along simple step edge. (c) plots the evolution of the surface Gibbs energy of an In droplet with four different contacting profiles at the step edge. Adapted from Ref. [48].

Fig. 10.  (Color online) (a) SEM image of an in-plane Si nanowire (SiNW) channel, led by an indium (In) droplet ahead. (b) presents the transfer properties of the devices measured at different VDS conditions, while the hole mobility in the SiNW channel under VDS = 1.0 V is extracted and plotted against VGS by the pink line. (c) Optical transmission spectra of the clean SiNWs after remnant a-Si:H etching, compared to those of the reference glass substrate, with a-Si:H coating and SiNWs without remnant a-Si:H etching, while (g) shows an optical image of the transparent poly-Si channels grown on glass substrate. SEM characterizations of the self-aligned poly-Si nanowire channels along the step edge lines are shown in (d), while a series of detailed HR-TEM analysis of a single nano-channel, transferred and mounted onto a copper grid are presented in (e)–(f). Adapted from Ref. [52].

Fig. 11.  (Color online) (a)–(d) show the fabrication procedure of line-shape engineered in-plane SiNWs.

Fig. 12.  (a)–(d) show the typical SEM images of the in-plane SiNWs grown into different step edge profile. The bright and thick vertical lines in (a) are the In stripes, which provide the source catalyst droplet formation. (d) shows a particular case that a single in-plane SiNWs grow to encompass an discrete island and leave it at the end following its entry path.

Fig. 13.  (Color online) [54] (a) SEM image of the in-plane SiNW spring, where a segment has been successfully picked up and transferred by a tungsten nano-probe to mount on both end, for mechanical testing. (b) and (c) show the SEM images of the initial and the stretched SiNW spring, while (d) and (e) present the mechanical analysis of the strain distribution in the SiNW segment. (f) shows the I–V characteristics measured on the c-Si nano spring channels, under squeezing or stretching states. The electric contacts between the SiNW spring and probe were realized by simple amorphous carbon coating. (g) shows the simulated force-displacement relationship of the SiNW spring.

[1]
Kim J, Salvatore G A, Araki H, et al. Stretchable optoelectronic systems for wireless optical characterization of the skin. Sci Adv, 2016, 2: e1600418 doi: 10.1126/sciadv.1600418
[2]
Xu B, Rogers J A. Mechanics-driven approaches to manufacturing—A perspective. Extrem Mech Lett, 2016, 7: 44 doi: 10.1016/j.eml.2015.12.012
[3]
Kim D H, Ghaffari R, Lu N, et al. Flexible and stretchable electronics for biointegrated devices. Ann Rev Biomed Eng, 2012, 14: 113 doi: 10.1146/annurev-bioeng-071811-150018
[4]
Hussain A M, Hussain M M. CMOS-technology-enabled flexible and stretchable electronics for internet of everything applications. Adv Mater, 2016, 28: 4219 doi: 10.1002/adma.v28.22
[5]
Hammock M L, Chortos A, Tee B C K, et al. The evolution of electronic skin (e-skin): a brief history, design considerations, and recent progress. Adv Mater, 2013, 25: 5997 doi: 10.1002/adma.201302240
[6]
Cheng T, Zhang Y, Lai. Stretchable thin-film electrodes for flexible electronics with high deformability and stretchability. Adv Mater, 2015, 27: 3349 doi: 10.1002/adma.v27.22
[7]
Wang Y, Zhu C, Pfattner R, et al. A highly stretchable, transparent, and conductive polymer. Sci Adv, 2017, 3: e1602076 doi: 10.1126/sciadv.1602076
[8]
Roberts M E, Mannsfeld S C B, Stoltenberg R M, et al. Flexible, plastic transistor-based chemical sensors. Org Electron, 2009, 10: 377 doi: 10.1016/j.orgel.2008.12.001
[9]
Sokolov A N, Roberts M E, Bao Z. Fabrication of low-cost electronic biosensors. Mater Today, 2009, 12: 12 doi: 10.1016/S1369-7021(09)70247-0
[10]
Arias A C, MacKenzie J D, McCulloch I, et al. Materials and applications for large area electronics: solution-based approaches. Chem Rev, 2010, 110: 3 doi: 10.1021/cr900150b
[11]
Lei Z, Wang Q, Sun S, et al. A bioinspired mineral hydrogel as a self-healable, mechanically adaptable ionic skin for highly sensitive pressure sensing. Adv Mater, 2017, 29: 1700321 doi: 10.1002/adma.201700321
[12]
Lin P, Yan F. Organic thin-film transistors for chemical and biological sensing. Adv Mater, 2012, 24: 34 doi: 10.1002/adma.201103334
[13]
Wang L, Liu P, Guan P, et al. In situ atomic-scale observation of continuous and reversible lattice deformation beyond the elastic limit. Nat Commun, 2013, 4: 2413 doi: 10.1038/ncomms3413
[14]
Wang L, Zheng K, Zhang Z, et al. Direct atomic-scale imaging about the mechanisms of ultralarge bent straining in Si nanowires. Nano Lett, 2011, 11: 2382 doi: 10.1021/nl200735p
[15]
Zheng K, Han X, Wang L, et al. Atomic mechanisms governing the elastic limit and the incipient plasticity of bending Si nanowires. Nano Lett, 2009, 9: 2471 doi: 10.1021/nl9012425
[16]
Zhu Y, Xu F, Qin Q, et al. Mechanical properties of vapor-liquid-solid synthesized silicon nanowires. Nano Lett, 2009, 9: 3934 doi: 10.1021/nl902132w
[17]
Khang D Y, Jiang H, Huang Y, et al. A stretchable form of single-crystal silicon for high-performance electronics on rubber substrates. Science, 2006, 311: 208 doi: 10.1126/science.1121401
[18]
Kim H W, Shim S H. Helical nanostructures of SiOx synthesized through the heating of Co-coated substrates. Appl Surf Sci, 2007, 253: 3664 doi: 10.1016/j.apsusc.2006.07.083
[19]
Zhang H F, Wang C M, Buck E C, et al. Synthesis, characterization, and manipulation of helical SiO2 nanosprings. Nano Lett, 2003, 3: 577 doi: 10.1021/nl0341180
[20]
Swain B S, Lee S S, Lee S H, et al. Transformation of silicon nanowires to nanocoils by annealing in reducing atmosphere. J Cryst Growth, 2011, 327: 276 doi: 10.1016/j.jcrysgro.2011.06.018
[21]
Tang Y H, Zhang Y F, Wang N, et al. Morphology of Si nanowires synthesized by high-temperature laser ablation. J Appl Phys, 1999, 85: 7981 doi: 10.1063/1.369389
[22]
Tian B, Xie P, Kempa T J, et al. Single-crystalline kinked semiconductor nanowire superstructures. Nat Nano, 2009, 4: 824 doi: 10.1038/nnano.2009.304
[23]
Lugstein A, Steinmair M, Hyun Y J, et al. Pressure-induced orientation control of the growth of epitaxial silicon nanowires. Nano Lett, 2008, 8: 2310 doi: 10.1021/nl8011006
[24]
Musin I R, Filler M A. Chemical control of semiconductor nanowire kinking and superstructure. Nano Lett, 2012, 12: 3363 doi: 10.1021/nl204065p
[25]
Schmidt V, Wittemann J V, Senz S, et al. Silicon nanowires: a review on aspects of their growth and their electrical properties. Adv Mater, 2009, 21: 2681 doi: 10.1002/adma.200803754
[26]
Wagner R S, Ellis W C. Vapor-liquid-solid mechanism of single crystal growth. Appl Phys Lett, 1964, 4: 89 doi: 10.1063/1.1753975
[27]
Xu F, Lu W, Zhu Y. Controlled 3D buckling of silicon nanowires for stretchable electronics. ACS Nano, 2011, 5: 672 doi: 10.1021/nn103189z
[28]
Kim D H, Ahn J H, Choi W M, et al. Stretchable and foldable silicon integrated circuits. Science, 2008, 320: 507 doi: 10.1126/science.1154367
[29]
Jang K I, Li K, Chung H U, et al. Self-assembled three dimensional network designs for soft electronics. Nat Commun, 2017, 8: 15894
[30]
Sepulveda A C C, Cordero M S D, Carreño A A A, et al. Stretchable and foldable silicon-based electronics. Appl Phys Lett, 2017, 110: 134103 doi: 10.1063/1.4979545
[31]
Rojas J P, Arevalo A, Foulds I G, et al. Design and characterization of ultra-stretchable monolithic silicon fabric. Appl Phys Lett, 2014, 105: 154101 doi: 10.1063/1.4898128
[32]
Kim J, Lee M, Shim H J, et al. Stretchable silicon nanoribbon electronics for skin prosthesis. Nat Commun, 2014, 5: 5747 doi: 10.1038/ncomms6747
[33]
Pevzner A, Engel Y, Elnathan R, et al. Confinement-guided shaping of semiconductor nanowires and nanoribbons: " writing with nanowires”. Nano Lett, 2012, 12: 7 doi: 10.1021/nl201527h
[34]
Gonzalez M, Axisa F, Bulcke M V, et al. Design of metal interconnects for stretchable electronic circuits. Microelectron Rel, 2008, 48: 825 doi: 10.1016/j.microrel.2008.03.025
[35]
Vanfleteren J, Gonzalez M, Bossuyt F, et al. Printed circuit board technology inspired stretchable circuits. MRS Bull, 2012, 37: 254 doi: 10.1557/mrs.2012.48
[36]
Yu L, Alet P J, Picardi G, et al. An in-plane solid-liquid-solid growth mode for self-avoiding lateral silicon nanowires. Phys Rev Lett, 2009, 102: 125501 doi: 10.1103/PhysRevLett.102.125501
[37]
Yu L, P Roca i Cabarrocas. Initial nucleation and growth of in-plane solid-liquid-solid silicon nanowires catalyzed by indium. Phys Rev B, 2009, 80: 085313 doi: 10.1103/PhysRevB.80.085313
[38]
Yu L, P Roca i Cabarrocas. Growth mechanism and dynamics of in-plane solid-liquid-solid silicon nanowires. Phys Rev B, 2010, 81: 085323 doi: 10.1103/PhysRevB.81.085323
[39]
Scarontich I, Car R, Parrinello M. Amorphous silicon studied by ab initio molecular dynamics: preparation, structure, and properties. Phys Rev B, 1991, 44: 11092 doi: 10.1103/PhysRevB.44.11092
[40]
Roorda S, Doorn S, Sinke W C, et al. Calorimetric evidence for structural relaxation in amorphous silicon. Phys Rev Lett, 1989, 62: 1880 doi: 10.1103/PhysRevLett.62.1880
[41]
Yu L P. Morphology control and growth dynamics of in-plane solid–liquid–solid silicon nanowires. Physica E, 2012, 44: 1045 doi: 10.1016/j.physe.2011.06.005
[42]
Xue Z, Xu M, Li X, et al. In-plane self-turning and twin dynamics renders large stretchability to mono-like zigzag silicon nanowire springs. Adv Func Mater, 2016, 26: 5352 doi: 10.1002/adfm.201600780
[43]
Xue Z, Xu M, Zhao Y, et al. Engineering island-chain silicon nanowires via a droplet mediated Plateau-Rayleigh transformation. Nat Commun, 2016, 7: 12836 doi: 10.1038/ncomms12836
[44]
Shin N, Chi M, Howe J Y, et al. Rational defect introduction in silicon nanowires. Nano Lett, 2013, 13: 1928 doi: 10.1021/nl3042728
[45]
Algra R E, Verheijen M A, Borgstrom M T, et al. Twinning superlattices in indium phosphide nanowires. Nature, 2008, 456: 369 doi: 10.1038/nature07570
[46]
Li X, Wei X, Xu T, et al. Remarkable and crystal-structure-dependent piezoelectric and piezoresistive effects of InAs nanowires. Adv Mater, 2015, 27: 2852 doi: 10.1002/adma.v27.18
[47]
Li X, Wei X L, Xu T T, et al. Mechanical properties of individual InAs nanowires studied by tensile tests. Appl Phys Lett, 2014, 104: 103110 doi: 10.1063/1.4868133
[48]
Xu M, Xue Z, Yu L, et al. Operating principles of in-plane silicon nanowires at simple step-edges. Nanoscale, 2015, 7: 5197 doi: 10.1039/C4NR06531J
[49]
Yu L, Moustapha O, Oudwan M, et al. Guided growth of in-plane lateral SiNWs led by indium catalysts. Mater Res Soc Symp Proc, 2009, 1178E: AA07
[50]
Yu L, Oudwan M, Moustapha O, et al. Guided growth of in-plane silicon nanowires. Appl Phys Lett, 2009, 95: 113106 doi: 10.1063/1.3227667
[51]
Yu L, Chen W, O'Donnell B, et al. Growth-in-place deployment of in-plane silicon nanowires. Appl Phys Lett, 2011, 99: 203104 doi: 10.1063/1.3659895
[52]
Xu M, Wang J, Xue Z, et al. High performance transparent in-plane silicon nanowire Fin-TFTs via a robust nano-droplet-scanning crystallization dynamics. Nanoscale, 2017, 9: 10350 doi: 10.1039/C7NR02825C
[53]
Chen W, Yu L, Misra S, et al. Incorporation and redistribution of impurities into silicon nanowires during metal-particle-assisted growth. Nat Commun, 2014, 5: 4134
[54]
Xue Z, Sun M, Zhao Y, et al. Deterministic line-shape programming of silicon nanowires for extremely stretchable springs and electronics. Nano Lett, 2017, 17: 7638
[55]
O'Mara W, Herring R B, Hunt L P. Handbook of semiconductor silicon technology. Crest Publishing House, 2007
  • Search

    Advanced Search >>

    GET CITATION

    shu

    Export: BibTex EndNote

    Article Metrics

    Article views: 6514 Times PDF downloads: 165 Times Cited by: 0 Times

    History

    Received: 06 October 2017 Revised: 01 December 2017 Online: Accepted Manuscript: 12 December 2017Published: 01 January 2018

    Catalog

      Email This Article

      User name:
      Email:*请输入正确邮箱
      Code:*验证码错误
      Zhaoguo Xue, Taige Dong, Zhimin Zhu, Yaolong Zhao, Ying Sun, Linwei Yu. Engineering in-plane silicon nanowire springs for highly stretchable electronics[J]. Journal of Semiconductors, 2018, 39(1): 011001. doi: 10.1088/1674-4926/39/1/011001 Z G Xue, T G Dong, Z M Zhu, Y L Zhao, Y Sun, L W Yu, Engineering in-plane silicon nanowire springs for highly stretchable electronics[J]. J. Semicond., 2018, 39(1): 011001. doi: 10.1088/1674-4926/39/1/011001.Export: BibTex EndNote
      Citation:
      Zhaoguo Xue, Taige Dong, Zhimin Zhu, Yaolong Zhao, Ying Sun, Linwei Yu. Engineering in-plane silicon nanowire springs for highly stretchable electronics[J]. Journal of Semiconductors, 2018, 39(1): 011001. doi: 10.1088/1674-4926/39/1/011001

      Z G Xue, T G Dong, Z M Zhu, Y L Zhao, Y Sun, L W Yu, Engineering in-plane silicon nanowire springs for highly stretchable electronics[J]. J. Semicond., 2018, 39(1): 011001. doi: 10.1088/1674-4926/39/1/011001.
      Export: BibTex EndNote

      Engineering in-plane silicon nanowire springs for highly stretchable electronics

      doi: 10.1088/1674-4926/39/1/011001
      Funds:

      Project supported by the National Basic Research 973 Program (No. 2014CB921101), the National Natural Science Foundation of China (No. 61674075), the National Key Research and Development Program of China (No. 2017YFA0205003), the Jiangsu Excellent Young Scholar Program (No. BK20160020), the Scientific and Technological Support Program in Jiangsu Province (No. BE2014147-2), the Jiangsu Shuangchuang Team's Personal Program and the Fundamental Research Funds for the Central Universities, and the China Scholarship Council and the Postgraduate Program of Jiangsu Province (No. KYZZ160052).

      More Information
      • Corresponding author: yulinwei@nju.edu.cn
      • Received Date: 2017-10-06
      • Revised Date: 2017-12-01
      • Published Date: 2018-01-01

      Catalog

        /

        DownLoad:  Full-Size Img  PowerPoint
        Return
        Return